1 a steel is heated until 85 austenite with a carbon content of 105 forms estimate the temperature and the overall
1 a steel contains 55 alpha and 45 gamma at 750degc estimate the carbon content of the steel2 a steel contains 96 gamma
1 a steel contains 8 cementite and 92 ferrite at room temperature estimate the carbon content of the steel is the steel
for an fe-115 c alloy determinea the temperature at which austenite first begins to transform on coolingb the primary
1 what is the dicurrenerence between cast iron and steels2 what do a1 a3 and acm temperatures refer to are these
you use an arc-welding process to join an eutectoid steel cooling rates may be very high following the joining process
an age-hardened al-cu bracket is used to hold a heavy electrical-sensing device on the outside of a steel-making
1 describe the changes in properties that occur upon the tempering of an eutectoid steel2 you wish to attach aluminum
1 fine pearlite and a small amount of martensite are found in a quenched 1080 steel what microstructure would be
1 you would like to produce a gray iron casting that freezes with no primary austenite or graphite if the carbon
occasionally when an austenitic stainless steel is welded the weld deposit may be slightly magnetic based on the
a steel bar is to be quenched in agitated water determine the maximum diameter of the bar that will produce a minimum
a 2-in-diameter bar of 4320 steel is to have a hardness of at least hrc 35 what is the minimum severity of the quench h
1 a 1080 steel is cooled at the fastest possible rate that still permits all pearlite to form what is this cooling rate
a part produced from a 4320 steel has a hardness of hrc 35 at a critical location after quenching determinea the
a steel part must have an as-quenched hardness of hrc 35 in order to avoid excessive-wear rates during use when the
1 define cast iron using the fe-fe3c phase diagram2 what are the different types of cast irons explain using a sketch3
1 what is a stainless steel why are stainless steels stainless2 we wish to produce a martensitic stainless steel
1 why is it that the strength of the heat-affected zone is higher for low-carbon steels what is the role of retained
a 1050 steel is welded after cooling hardnesses in the heat-affected zone are obtained at various locations from the
1 design a heat treatment for a hook made of 1-in-diameter steel rod having a microstructure containing a mixture of
1 a quenched and tempered 10110 steel is found to have surface cracks that cause the heattreated part to be rejected by
1 a explain how pure copper is madeb what are some of the important properties of copperc what is brassd what is
1 compare the percentage increase in the yield strength of commercially pure annealed aluminum magnesium and copper by