You are considering two different diffusion processes involving Carbon into FCC iron. The first process is carried out at 900 oC for 3 hours and produces a carbon concentration of 0.20 wt% at a depth of 2 mm. At what depth would this concentration occur if a similar process at 1100oC for 2 hours was performed (on the same type of steel with the same surface concentration of carbon applied)?