It is desirable to produce a copper-nickel alloy that has a minimum noncold-worked tensile strength of 390 Mpa and a ductility of at least 40% elongation. Is such an alloy possible? If so, what must be its composition? If this is not possible, then explain why.
Note: Be sure to provide supporting data to back-up your statements.